EMBLEM Solvent Polymeric Lamination Film Matt
SOPOLAMMA5-76Normal pris 895,00 kr Gem Liquid error (product-template line 120): -Infinity%
Laminating films of our EMBLEM SOPOLAM 5 series are self-adhesive PVC films for finishing process and graphic industry. The pressure sensitive glue allows a fast and effective workflow during lamination process from roll.
Material: PVC, polymeric
Thickness: 75 µm
Adhesive: high transparency, permanent, solvent-free acrylate
Liner: glassine paper 72 g/m², siliconized
Adhesion power on glass: 14 N / 25 mm - acc. to FINAT 1 - 24h contact (average value)
Temperature resistance: - 30°C to + 80°C
Application temperature: min. + 10°C
Flame retardant: self extinguishing, tested on steel
Standard roll width: 76 cm, 105 cm, 137,2 cm and 152,4 cm
Standard roll length: 50 m
Lamination film: face out
Durability: 5 years under condition of Middle European climate
Storage: at 15°C - 25°C, 50% rel. humidity
Shelf life: 24 month in original boxes
SOPOLAMMA5 gives a uniform matt non-reflecting surface to the print and protects them from abrasion, humidity and slight mechanical influences.
In order to avoid bleaching from the prints EMBLEM SOPOLAMMA5 has a UV protector. The lamination film can be used for in- and outdoor applications and has best characteristics against yellowing.
To avoid mechanical influences lamination is advisable at all. The lamination can be done right to edges or over the edges. The user should check before using what is more appropriate. We recommend a lamination process with overlap of approx. 3 mm when critical printing medias are used.
EMBLEM SOPOLAMMA5 lamination films are for dry application processing. The lifetime of SOPOLAMMA5 is up to 5 years. Please pay attention that the lifetime of the laminated print is related to much more other facts so the end user has to make his own tests. To avoid fingerprints the use of cotton-gloves is advisable.
We recommend to use polymeric self-adhesive film EMBLEM SOFOGLP 5 series for printing in addition to SOPOLAM 5 series lamination film.